Lupoy® GP5001AF
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kIlIaP_Lupoy-GP5001AF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupoy® GP5001AF is a Polycarbonate + ABS (PC+ABS) material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Lupoy® GP5001AF are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 117 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 58.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 100 | % | ASTM D638 |
| Flexural Modulus | 2400 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 96.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 490 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 105 | °C | ASTM D648 |
| CLTE - Flow | 8.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 9.0E-3 | ASTM D150 | |
| Arc Resistance (1.59 mm) | 100 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 220 to 235 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 235 to 245 | °C | |
| Nozzle Temperature | 235 to 250 | °C | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 58.8 to 118 | MPa | |
| Back Pressure | 0.00 to 3.92 | MPa | |
| Screw Speed | 40 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 810CI | Salflex Polymers Ltd. | PP Copolymer | Salflex |
| SuperLite® SL551400-100 (2.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Celstran® PA66-GF50-02-Natural | Celanese Corporation | Nylon 66 | Celstran® |
| HIVOREX J2200 | Lotte Chemical Corporation | HDPE | HIVOREX |
| PPO™ 646 resin | SABIC Innovative Plastics | PPE+PS | PPO™ |