Moplen EP600V
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kHqOw4_Moplen-EP600V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Moplen EP600V is an ultra high fluidity, heterophasic copolymer, suitable for thin walled injection moulding applications and as base resin for compounding applications. The product combines a good stiffness with good impact resistance, even at sub-zero temperatures. In addition a good dimensional stability is given. Moplen EP600V is used for items with long flow paths as well as for long glass fibre reinforced recipes (GMT/LFT). Moplen EP600V contains neither nucleation agents nor antistaticums or slip/antiblock agents. For regulatory compliance information see Moplen EP600V Regulatory Affairs Product Stewardship Information/Certification Data Sheet (RAPIDS) It is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 100 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 135 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 72 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 30.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 7.0 | % | |
| Break | 10 | % | |
| Flexural Modulus - 1% Secant 1(23°C) | 1450 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 152 | °C | ISO 306/A50 |
| Accelerated Oven Ageing 2(150°C) | 360 | hr | ISO 4577 |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | Forced Circulation |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bynel® 3101 | DuPont Packaging & Industrial Polymers | EVA | Bynel® |
| Hostacom SB224-1 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Hyundai EP PA6 LS630 | HYUNDAI EP Co., Ltd. | Nylon 6 | Hyundai EP PA6 |
| Lucent PP TPP-320 | Lucent Polymers, Inc. | PP, Unspecified | Lucent PP |
| PENTAMID A GV15 MK15 H RC schwarz | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |