| Glass fiber reinforced grades-20% Glass fiber, Frictional wear resistant grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 4.00 mm | 0.40 to 0.60 | % | |
| Flow : 4.00 mm | 0.10 to 0.30 | % | |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 5500 | MPa | ISO 178 |
| Flexural Stress 2 | 133 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 43 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 149 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 146 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 152 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 3.0E-5 | cm/cm/°C | |
| Transverse | 6.0E-5 | cm/cm/°C | |
| RTI Elec (1.50 mm) | 130 | °C | UL 746 |
| RTI Imp (1.50 mm) | 120 | °C | UL 746 |
| RTI Str (1.50 mm) | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength 3 | 35 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.40 | ||
| 1 MHz | 3.40 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.0E-3 | ||
| 1 MHz | 9.0E-3 | ||
| Comparative Tracking Index | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.380 mm | V-2 | ||
| 3.00 mm | V-1 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | short time test |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra PC HF UV | ResMart | PC | ResMart Ultra |
| Miflon® 2333B | Jiangsu Meilan Chemical Co., Ltd. | PTFE | Miflon® |
| Vi-Chem PVC V142-70 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Vamac® GXF | DuPont Performance Elastomers | AEM | Vamac® |
| Lucofin® 1414-t1 | Lucobit AG | Polyolefin, Unspecified | Lucofin® |