PC/ABS alloy medium-high thermal resistance, good flow and mechanical properties, low moisture absorption and good dimensional stability. FIAT CR 110.500 - FORD TL 522 31 (Type B) Available: all colors, UV stabilized (L). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 to 1.15 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 to 0.70 | % | |
| Across Flow | 0.40 to 0.70 | % | |
| Water Absorption | ASTM D570, ISO 62 | ||
| 23°C, 24 hr | 0.20 | % | |
| Saturation, 23°C | 0.60 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 50.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 50 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2150 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 80.0 | MPa | ISO 178 |
| Break | 80.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 30 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 2(23°C) | No Break | ASTM D256, ISO 179 | |
| Notched Izod Impact (23°C, 3.20 mm) | 550 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 118 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature 3 | 90.0 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 130 | °C | ASTM D1525, ISO 306/A50 4 4 |
| -- | 125 | °C | ASTM D1525, ISO 306/B50 5 5 |
| Ball Pressure Test (125°C) | Pass | VDE 0470 | |
| CLTE - Flow (-30 to 30°C) | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 24 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Oxygen Index | 23 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 6x4x50 mm |
| 3 . | 20000 hrs |
| 4 . | Rate A (50°C/h), Loading 1 (10 N) |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vital-Line SHE5205G | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Karina WHITE PVC COMPOUND -E 898-10/137-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| INSPIRE™ T710-25 ES | Trinseo | PP, Unspecified | INSPIRE™ |
| Hostacom TRC 333N G62641 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 2912-60 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |