Generic Nylon Copolymer
| Category: | Nylon Copolymer , Polyamide Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kGeXIg_Generic-Nylon-Copolymer.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon Copolymer This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 to 1.14 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation | |||
| Break, 23°C | 5.0 to 500 | % | ASTM D638 |
| Break, 23°C | 7.0 to 50 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2840 to 3500 | MPa | ASTM D790 |
| 23°C | 2500 to 5500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 69.9 to 138 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 to 35 | kJ/m² | ISO 179 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 to 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+11 to 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength (23°C) | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity (23°C) | 6.50 | IEC 60250 | |
| Dissipation Factor (23°C) | 0.070 to 0.50 | IEC 60250 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 100 GB 40 | RTP Company | PP, Unspecified | RTP |
| Small Boss RPVC03 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | PVC, Rigid | Small Boss |
| ALCUDIA® LDPE 2202-F | REPSOL | LDPE | ALCUDIA® LDPE |
| PENTAMID B GV30 H LS natural | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |
| ExxonMobil™ LLDPE LL 1001 Series | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |