TECHNYL® A 218 MT15 V25 BLACK 21 N
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kGOgfg_TECHNYL-A-218-MT15-V25-BLACK-21-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66 , reinforced with 25% of glass fibre and 15% of mineral filler , heat stabilized , for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.47 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.2 | -- | % | |
| Flow | 0.65 | -- | % | |
| Water Absorption (23°C, 24 hr) | 1.4 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.540 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 5500 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 140 | 100 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 2.4 | 5.0 | % | ISO 527-2/1A |
| Flexural Modulus | 8500 | 5000 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 45 | 80 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 4.0 | 6.5 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 240 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 263 | -- | °C | ISO 11357-3 |
| CLTE - Transverse (23 to 85°C) | 3.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 5.0E+14 | 3.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 3.0E+15 | 3.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 35 | 35 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.70 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.080 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 425 | 425 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 265 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PPR ABS04 | Premier Plastic Resins, Inc. | ABS | PPR |
| Viton® VTR-8802 | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| CYCOLOY™ C2950 resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |
| LARIPUR® LPR 7060 | COIM S.p.A. | TPU-Polyether | LARIPUR® |
| Karina IVORY PVC COMPOUND -E 807D35/ 1-C-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |