ADENE NCJA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | A.D. Compound spa |
| Trademark: | ADENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kGIVwV_ADENE-NCJA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ADENE NCJA is a Polypropylene Homopolymer (PP Homopolymer) material filled with 30% calcium carbonate. It is available in Europe or North America. Primary attribute of ADENE NCJA: Homopolymer. Typical application of ADENE NCJA: Consumer Goods |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Ash Content | 30 | % | ISO 3451-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 23.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 7.0 | % | |
| Break | 45 | % | |
| Flexural Modulus | 1850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 3.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 12 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 63.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 94.0 | °C | ISO 306/B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PPX-G30-(color)N | Polymer Resources Ltd. | PPE+PS | PRL |
| Varcum 29607 | Durez Corporation | Phenolic | Varcum |
| DENIBLEND E | Vamp Tech | PC+ABS | DENIBLEND |
| KRYSTALFLEX™ PE393 | Huntsman Corporation | PUR-Eth,aliphat | KRYSTALFLEX™ |
| Karina BLACK PVC COMPOUND -E CAK 60-48/ 1-F | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |