PBT, 40% mineral reinforced, food grade |
General Information | |
---|---|
Filler / Reinforcement |
|
Features |
|
Resin ID (ISO 1043) |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 1.81 | g/cm³ | ISO 1183 |
Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 45 | g/10 min | ISO 1133 |
Molding Shrinkage | ISO 294-4 | ||
Across Flow | 1.4 | % | |
Flow | 1.5 | % | |
Water Absorption (Equilibrium, 23°C, 50% RH) | 0.15 | % | Internal Method |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus | 4000 | MPa | ISO 527-2 |
Tensile Stress (Break) | 45.0 | MPa | ISO 527-2 |
Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Unnotched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eU |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Melting Temperature 1 | 225 | °C | ISO 11357-3 |
Electrical | Nominal Value | Unit | Test Method |
---|---|---|---|
Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
Flammability | Nominal Value | Unit | Test Method |
---|---|---|---|
Flammability Classification 2(0.800 mm) | HB | IEC 60695-11-10, -20 |
Note Message | |
---|---|
1 . | 10°C/min |
2 . | UL Registered |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
RAMAPET® N2 | Indorama Ventures PCL | PET | RAMAPET® |
TEKNIFLEX® VA10300 ALU | Tekni-Films, a div of Tekni-Plex | Film, PVC/PCTFE | TEKNIFLEX® |
Moplen EP201N | LyondellBasell Industries | PP Impact Copolymer | Moplen |
Cheng Yu 3213 | Cheng Yu Plastic Company Limited | TPE | Cheng Yu |
Durez® 32025B | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |