Toyolac® PX10 X06
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Plastics (Malaysia) Sdn. Bhd. |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kFvnEK_Toyolac-PX10-X06.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toyolac® PX10 X06 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or Europe. Important attributes of Toyolac® PX10 X06 are:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.15 | g/cm³ | ASTM D792 |
| 23°C | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (23°C) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- 1 | 54.0 | MPa | ASTM D638 |
| -- | 59.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 2 | > 50 | % | ASTM D638 |
| Break | > 50 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 3 | 2090 | MPa | ASTM D790 |
| -- 4 | 2140 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 5 | 82.0 | MPa | ASTM D790 |
| -- 6 | 87.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 48 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C, 12.7 mm) | 490 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 120 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 7 | 116 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 3.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vipel® F010-BNT-00 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| TOTAL Polyethylene MDPE HT 514 | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
| NuSil MED-4917 | NuSil Technology | Silicone | NuSil |
| Kepital® F30-02 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| KOCETAL® UR302BK | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |