OnForce™ LFT UR-40 LGF/000 Natural
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | PolyOne Corporation |
| Trademark: | OnForce™ LFT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kFgG96_OnForce-LFT-UR-40-LGF-000-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyvan's long fiber thermoplastic polymers are used in situations where high hardness and good impact resistance are required, such as metal substitution or other structural applications. These products exhibit enhanced physical and mechanical properties compared to staple fiber products. Its advantages include improved impact strength, elasticity and material strength in different temperature ranges. In addition, compared with traditional high-filled short fiber products, long fiber thermoplastic polymers show improved properties in terms of creep and fatigue resistance, improved dimensional stability and unique surface finish. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 11000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 221 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.0 - 3.0 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 307 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 370 | J/m | ASTM D256 |
| Unnotched Izod Impact | 1400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 113 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 90.0 | °C | |
| Drying Time | 8.0 - 12 | hr | |
| Processing (Melt) Temp | 220 - 250 | °C | |
| Mold Temperature | 80.0 | °C |
| Injection instructions |
|---|
| LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.This grade must be dried in a dessicant dryer with a dew point set at -40°C. |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® HJ4012 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| Badamid® LA70 GF30 H | Bada AG | Nylon 66 | Badamid® |
| BUP 643 | Bonyan Kala Chemie Company | Polyester, TS | BUP |
| ASTADUR™ PBT B4500 | Marplex Australia Pty. Ltd. | PBT | ASTADUR™ |
| Sylvin 4200-88UV Red 6287 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |