PRE-ELEC® PE 1201
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kDyitB_PRE-ELEC-PE-1201.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® PE 1201 is a conductive thermoplastic compound based on PE-HD. The electrical conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PE 1201 has an excellent balance of mechanical properties and is easy to extrude. Typical applications include extrusion of monolayer pressure pipes (PE 80) for areas with explosive atmosphere and sheets which can be welded or vacuum formed without pre-drying. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.996 | g/cm³ | ASTM D792 |
| -- | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 3.0 - 4.0 | % | ASTM D955 |
| Flow direction | 3.0 - 4.0 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 26.0 | MPa | ASTM D638, ISO 527-2 |
| -- | 12.0 | MPa | ASTM D638 |
| 4.00 mm | 12.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 12 | % | ASTM D638, ISO 527-2 |
| Fracture | 26 | % | ASTM D638 |
| Fracture, 4.00mm | 26 | % | ISO 527-2 |
| Flexural Modulus (4.00 mm) | 1150 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | 6.30 | kJ/m² | ASTM D256 |
| 23°C, 4.00 mm | 12.6 | kJ/m² | ASTM D256 |
| Notched Izod Impact 1 | ISO 180 | ||
| -20°C | 5.7 | kJ/m² | ISO 180 |
| 23°C | 12 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ASTM D256 | |
| 23°C, 4.00 mm | No Break | ASTM D256 | |
| Unnotched Izod Impact Strength 2 | ISO 180 | ||
| -20°C | No Break | ISO 180 | |
| 23°C | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 77.2 | °C | ASTM D1525 3 |
| -- | 126 | °C | ASTM D1525, ISO 306/A50 4 4 |
| -- | 77.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+5 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Volume Resistivity | < 1.0E+3 | ohms·cm | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 200 | °C | |
| Cylinder Zone 2 Temp. | 210 | °C | |
| Cylinder Zone 3 Temp. | 220 | °C | |
| Cylinder Zone 4 Temp. | 220 | °C | |
| Cylinder Zone 5 Temp. | 230 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 230°C |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | 标准 B (120°C/h), 载荷2 (50N) |
| 4 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2909-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Abstron IM17A | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Andur 85 APLF | Anderson Development Company | PUR-Ether/TDI | Andur |
| Ebalta AH 100 / SR | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| ENVIROPLAS® ENV13-NC160 | ENVIROPLAS®, Inc. | PC | ENVIROPLAS® |