Syncure™ S1060A Natural
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Syncure™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kDwaCo_Syncure-S1060A-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Moisture cross-linked polyethylene composite material. Base resin composition, used in the Syncure system of Plivan. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Apparent Density 1 | 0.50 | g/cm³ | Internal method |
| Melt Mass-Flow Rate (MFR) 2(190°C/2.16 kg) | 0.73 | g/10 min | ASTM D1238 |
| Gel Content 3 | 75 | % | ASTM D2765 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deformation 4(131°C) | 5.7 | % | UL 1581 |
| Thermal creep elongation 5 | 45 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 6 | 11.0 | MPa | ASTM D638 |
| Tensile Strength 7(Break) | 16.5 | MPa | ASTM D638 |
| Tensile Elongation 8(Break) | 600 | % | ASTM D638 |
| Additional Information |
|---|
| 张力、伸长率、变形值、热蠕变和凝胶值基于95 phr S1060A / 5 phr S1000B系统测量得出；并在90摄氏度的水中硫化6小时。颗粒外观为 1/8"圆柱状。 |
| Note Message | |
|---|---|
| 1 . | Geon® 1169 |
| 2 . | Procedure A |
| 3 . | Cross-linked PE, Method B (Non-Arbitration Test) |
| 4 . | 500g,1 hour |
| 5 . | SYV-40 |
| 6 . | Type 4, 510mm/min |
| 7 . | Type 4, 510mm/min |
| 8 . | Type 4, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| McCann PP M30GHPPCC | McCann Plastics Inc. | PP Homopolymer | McCann PP |
| TAROLOX 10 Z1 G4 | Taro Plast S.p.A. | PBT | TAROLOX |
| ECP 110 | TBA Electro Conductive Products Ltd. | PP, Unspecified | ECP |
| Sinpolene GPP5625 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | SINPOLENE |
| Hifax TRC 495P G13076 | LyondellBasell Industries | PP Copolymer | Hifax |