VECTRA® A515

Category:	LCP , Liquid Crystal Polymer
Manufacturer:	Celanese Corporation
Trademark:	VECTRA®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	kCvsoQ_VECTRA-A515.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Easier flow and slightly improved toughness over A530. Outstanding hydrolytic stability. 15% mineral filled.

Chemical abbreviation according to ISO 1043-1 : LCP
Inherently flame retardant
FDA compliant
UL-Listing V-0 in natural at 0.38mm thickness per UL 94 flame testing.

Relative-Temperature-Index (RTI) according to UL 746B: electrical 130°C, mechanical 130°C.

UL = Underwriters Laboratories (USA)

General Information
Filler / Reinforcement	Mineral filler, 15% filler by weight
Features	Good liquidity Hydrolysis resistance Halogen-free Flame retardancy
Agency Ratings	EU 2002/96/EC (WEEE) FDA not rated
RoHS Compliance	Contact manufacturer
Forms	Particle
Processing Method	Injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1)
Resin ID (ISO 1043)	LCP

Physical	Nominal Value	Unit	Test Method
Density
--	1.52	g/cm³	ISO 1183
--	1520	kg/m³	ISO 1183 ¹
Molding Shrinkage
Vertical flow direction	0.60	%	ISO 294-4
Flow direction	0.0	%	ISO 294-4
Flow	0.0	%	ISO 2577 ²
Transverse flow	0.60	%	ISO 2577 ³

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	63		ISO 2039-2

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	10500	MPa	ISO 527-2/1A/1
Tensile Stress (Break)	175	MPa	ISO 527-2/1A/5
Tensile Strain (Break)	4.5	%	ISO 527-2/1A/5
Flexural Modulus (23°C)	11000	MPa	ISO 178
Flexural Stress (23°C)	175	MPa	ISO 178
Compressive Modulus	9500	MPa	ISO 604
Compressive Stress (1% Strain)	61.0	MPa	ISO 604

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength
23°C	59	kJ/m²	ISO 179/1eA
23°C	59.0	kJ/m²	ISO 179/1eA ⁴
Charpy Unnotched Impact Strength (23°C)	100	kJ/m²	ISO 179/1eU
Notched Izod Impact (23°C)	60	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength (23°C)	130	kJ/m²	ISO 180/1U

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	232	°C	ISO 75-2/B
0.45 MPa	232	°C	ISO 75-2 ⁵
1.8 MPa, not annealed	185	°C	ISO 75-2/A
1.8 MPa	185	°C	ISO 75-2 ⁶
8.0 MPa, not annealed	103	°C	ISO 75-2/C
8.0 MPa	103	°C	ISO 75-2 ⁷
Vicat Softening Temperature
--	149	°C	ISO 306/B50
50°C/h, B (50N)	149	°C	ISO 306 ⁸
Melting Temperature
-- ⁹	280	°C	ISO 11357-3
-- ¹⁰	280	°C	ISO 11357-3 ¹¹
CLTE - Transverse	3.0E-5	cm/cm/°C	ISO 11359-2

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+15	ohms	IEC 60093
Volume Resistivity
--	1.0E+15	ohms·cm	IEC 60093
--	1.0E+13	ohms·m	IEC 60093 ¹²
Dielectric Strength	40	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
100 Hz	3.80		IEC 60250
1 MHz	3.20		IEC 60250
Dissipation Factor			IEC 60250
100 Hz	0.010		IEC 60250
1 MHz	0.020		IEC 60250
Arc Resistance	145	sec	Internal method
Comparative Tracking Index
--	175	V	IEC 60112
--	175		IEC 60112 ¹³

Flammability	Nominal Value	Unit	Test Method
Flame Rating	V-0		UL 94

Injection	Nominal Value	Unit
Drying Temperature	150	°C
Drying Time	4.0 - 6.0	hr
Suggested Max Moisture	0.010	%
Hopper Temperature	20.0 - 30.0	°C
Rear Temperature	270 - 280	°C
Middle Temperature	275 - 285	°C
Front Temperature	280 - 290	°C
Nozzle Temperature	290 - 300	°C
Processing (Melt) Temp	285 - 295	°C
Mold Temperature	80.0 - 120	°C
Injection Pressure	50.0 - 150	MPa
Injection Rate	Fast
Holding Pressure	50.0 - 150	MPa
Back Pressure	0.00 - 3.00	MPa

Injection instructions
Manifold Temperature: 285 to 295°CZone 4 Temperature: 285 to 295°CFeed Temperature: 60 to 80°C

Note Message
1 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
2 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
3 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
4 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
5 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
6 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
7 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
8 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
9 .	10°C/min
10 .	10 °C/min
11 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
12 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???
13 .	??????,?? ISO 10350 ??? 23°C/50%r.h. ???

Resin Grade	Manufacturer	Category	Trademark
Spartech Polycom RJ72470	Spartech Polycom	PVC Alloy	Spartech
Wellamid® GF43-66/6 XE-NBK1	Wellman Engineering Resins	Nylon 66/6	Wellamid®
CompaDur® 125 GF 15 natural (014)	DimeLika Plast GmbH	PBT+PET	CompaDur®
Ecomass® 1050CO94	Ecomass Technologies	Nylon 12	Ecomass®
PLEXIGLAS® Film 0F008	Evonik Industries AG	Film, PMMA	PLEXIGLAS® Film