TAIRIREX GP525N
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAIRIREX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kBzmCE_TAIRIREX-GP525N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FCFC PS resin GP525N meets the requirements of UL, SGS and the certificates of environmental protection. |
| General Information | |
|---|---|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 | g/cm³ | ASTM D792 |
| 23°C | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 7.0 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| 23°C | 42.2 | MPa | ASTM D638 |
| 23°C | 42.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break, 23°C) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (23°C) | 3330 | MPa | ASTM D790, ISO 178 |
| Flexural Strength (23°C) | 78.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C, 6.35 mm) | 17 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1(1.8 MPa, Annealed, 3.18 mm) | 87.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525, ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ALL) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Residual Monomer | < 700 | ppm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 | °C | |
| Drying Time | 1.0 to 2.0 | hr | |
| Hopper Temperature | 40.0 | °C | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 195 | °C | |
| Front Temperature | 205 | °C | |
| Nozzle Temperature | 200 | °C | |
| Processing (Melt) Temp | 170 to 215 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 80°Cx2Hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BLUESTAR® POM BS270 | Shanghai BlueStar New Chemical Materials Co., Ltd. | Acetal (POM) Copolymer | BLUESTAR® POM |
| Electrafil® PS-31/EC | Techmer Engineered Solutions | PS (GPPS) | Electrafil® |
| Hostaform® MT24F01 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| PolyFibra® PF-PEF04 | FuturaMat | PP, Unspecified | PolyFibra® |
| NORYL GTX™ GTX840 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |