DuPure® TR 76 V
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Ducor Petrochemicals BV |
| Trademark: | DuPure® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kBrp5F_DuPure-TR-76-V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description DuPure TR 76 V is a controlled rheology modified heterophasic polypropylene copolymer. The product shows an excellent fluidity combined with a narrow molecular weight distribution, resulting in fast cycle-times and a high dimensional stability. Applications DuPure TR 76 V is suitable for: thin-walled packaging, buckets, housewares. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/30) | 45.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 7.0 | % | |
| Break | > 50 | % | |
| Shear Modulus | 530 | MPa | ISO 6721-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 6.5 | kJ/m² | |
| -20°C | 7.0 | kJ/m² | |
| 0°C | 9.0 | kJ/m² | |
| 23°C, Partial Break | 43 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 140 | kJ/m² | |
| -20°C | 190 | kJ/m² | |
| 0°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 4.0 | kJ/m² | |
| -20°C | 5.0 | kJ/m² | |
| 0°C | 7.0 | kJ/m² | |
| 23°C | 30 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 78.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 48.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 142 | °C | ISO 306/A |
| -- | 56.0 | °C | ISO 306/B |
| Melting Temperature (DSC) | 163 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene P254-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Telcar® TL-2575A | Teknor Apex Company | TPE | Telcar® |
| Zythane® 4070D | Alliance Polymers & Services | TPU-Polyester | Zythane® |
| HONES® PPS HS-CT30-G | Guangdong Shunde Hones Polymer Material Co., Ltd. | PPS | HONES® |
| SABIC® PPcompound 9154 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |