Greenflex® FF 35 F
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Greenflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kBdntg_Greenflex-FF-35-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Greenflex FF 35 F is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. The resin shows good stretchability and sealability. Main Application Greenflex FF 35 F is suitable for flexible packaging film having good fracture mechanical properties, for stretch hood packaging and profiles extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.929 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ISO 1133 |
| Vinyl Acetate Content | 9.0 | wt% | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, Injection Molded | 94 | ||
| Shore D, Injection Molded | 42 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 50 to 200 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : Blown Film | 95.0 | MPa | |
| 1% Secant, TD : Blown Film | 97.0 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, Blown Film | 7.00 | MPa | |
| TD : Yield, Blown Film | 6.00 | MPa | |
| MD : Break, Blown Film | 27.0 | MPa | |
| TD : Break, Blown Film | 28.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, Blown Film | 480 | % | |
| TD : Break, Blown Film | 650 | % | |
| Dart Drop Impact 1(Blown Film) | 550 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD | 20.0 | kN/m | |
| TD | 40.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 75.0 | °C | ISO 306/A |
| Melting Temperature | 102 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, Blown Film) | 65 | ASTM D2457 | |
| Haze (Blown Film) | 6.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® K306 | Chevron Phillips Chemical Company LLC | MDPE | Marlex® |
| Sinvicomp SIM5029R | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| TEKNIFLEX® MED 3014-0200 | Tekni-Films, a div of Tekni-Plex | Film, PP | TEKNIFLEX® MED |
| Arnitel® CM600-V | DSM Engineering Plastics | TPC-ES | Arnitel® |
| Sylvin 9302-70 Brown 7380 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |