RTP 102 GB 15
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kB6KcL_RTP-102-GB-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4830 | MPa | ASTM D638 |
| Tensile Strength | 41.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 3450 | MPa | ASTM D790 |
| Flexural Strength | 62.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 320 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 143 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 132 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm, Values per RTP Company testing.) | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, ASTM D-955, 0.25in: 7mil/in. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 218 - 274 | °C | |
| Middle Temperature | 218 - 274 | °C | |
| Front Temperature | 218 - 274 | °C | |
| Mold Temperature | 32.2 - 65.6 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® BGK 15 Natural | Radici Plastics | Nylon 6 | Radilon® |
| RONFALIN® C C130 U | A. Schulman Europe | PC+ABS | RONFALIN® C |
| Tarnamid® T-27 GF 20 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| EVALENE® PP PHJ1502 | JG Summit Petrochemical Corporation | PP Homopolymer | EVALENE® PP |
| ENGAGE™ 8842 | The Dow Chemical Company | TPO (POE) | ENGAGE™ |