PRE-ELEC® PP 1352
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kAzLyX_PRE-ELEC-PP-1352.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PRE-ELEC® PP 1352 is a dissipative thermoplastic compound based on polypropylene. The electrical dissipation is achieved by using special conductive carbon black. In addition to stable surface resistance between 1e5 to 1e8 ohms. PRE-ELEC® PP 1352 has an excellent balance of mechanical properties and is easy to injection mould. Typical applications include injection moulded dissipative ESD products such as crates, boxes and tote bins. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.969 | g/cm³ | ASTM D792 |
| -- | 0.980 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.2 to 1.8 | % | ASTM D955, ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore A | 96 | ||
| Shore D | 71 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 26.2 | MPa | ASTM D638 |
| Yield | 26.0 | MPa | ISO 527-2 |
| -- | 17.9 | MPa | ASTM D638 |
| 4.00 mm | 18.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 10 | % | |
| Break, 4.00 mm | 30 | % | |
| Flexural Modulus | |||
| 4.00 mm | 1380 | MPa | ASTM D790 |
| 4.00 mm | 1400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1 | |||
| -20°C | 4.2 | kJ/m² | ASTM D256 |
| -20°C | 5.0 | kJ/m² | ISO 179 |
| 23°C | 27 | kJ/m² | ISO 179, ASTM D256 |
| Charpy Unnotched Impact Strength 2 | |||
| -20°C | No Break | ASTM D256, ISO 179 | |
| 23°C | No Break | ISO 179, ASTM D256 | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | 2.10 | kJ/m² | |
| 23°C, 4.00 mm | No Break | ||
| Notched Izod Impact Strength 3 | ISO 180 | ||
| -20°C | 3.0 | kJ/m² | |
| 23°C | No Break | ||
| Unnotched Izod Impact (Area) | ASTM D256 | ||
| -20°C, 4.00 mm | No Break | ||
| 23°C, 4.00 mm | No Break | ||
| Unnotched Izod Impact Strength 4 | ISO 180 | ||
| -20°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 82.8 | °C | ASTM D648B |
| 0.45 MPa, Unannealed | 83.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 53.9 | °C | ASTM D648A |
| 1.8 MPa, Unannealed | 54.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 150 | °C | ISO 306/A50, ASTM D1525 5 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+5 to 1.0E+8 | ohms | IEC 61340-2-3 |
| Volume Resistivity | 1.0E+3 to 1.0E+7 | ohms·cm | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 80.0 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | 4 mm thickness |
| 4 . | 4 mm thickness |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Q310 (On-spec.) | SINOPEC Shanghai Petrochemical Co. Ltd. | LDPE | Sanren |
| Shin-Etsu Elastomer KEG-2000-40A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Cogegum® GFR/340 | Solvay Specialty Polymers | Polyolefin, Unspecified | Cogegum® |
| Jackdaw PP EP16BK6600 | Jackdaw Polymers | PP Homopolymer | Jackdaw PP |
| Sarlink® TPE ML-1680N NAT (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |