Crastin® T841FR NC010
| Category: | PBT , THERMOPLASTIC POLYESTER RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Crastin® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kAuQIb_Crastin-T841FR-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% Glass Reinforced, Flame Retardant, ToughenedPolybutylene Terephthalate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.54 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.2 | % | |
| Flow | 0.70 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.35 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.7 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 3000 | MPa | |
| 1000 hr | 2000 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | 8.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 46 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, Unannealed | 170 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 66.0 | °C | ISO 75-2/C |
| Vicat Softening Temperature | 180 | °C | ISO 306/B50 |
| Melting Temperature 1 | 205 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 27 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.00 | ||
| 1 MHz | 3.80 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.010 | ||
| 1 MHz | 0.018 | ||
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| Oxygen Index | 30 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density | 1.31 | g/cm³ | |
| Melt Viscosity (250°C, 1000 sec^-1) | 240 | Pa·s | ISO 11443 |
| Specific Heat Capacity of Melt | 1970 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.23 | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205F TFE 20 | RTP Company | Nylon 12 | RTP |
| Tecomid® NBX0 HF75 NL | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| Sylvin 9067-70 NATURAL | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Karina CLEAR PVC COMPOUND 75/202 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ALCUDIA® LDPE CP-104 | REPSOL | LDPE | ALCUDIA® LDPE |