VAMPAMID 66 3028 V0 HF
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPAMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kAtZn8_VAMPAMID-66-3028-V0-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UL 94 V0, 30 % glass fiber, halogen and red phosphorus free, with Vamp Tech F.R. system, excellent mechanical properties, GWFI 960/1-2, GWIT 775/1-2. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | |
| Across Flow | 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 170 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.1 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 7.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 250 | °C | ASTM D648A |
| Vicat Softening Temperature | 245 | °C | ASTM D1525 1 |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 140 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 425 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 to 2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.00 to 2.00 mm) | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 275 | °C | |
| Mold Temperature | 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRIBIT® 1551GN30 | Samyang Corporation | PBT | TRIBIT® |
| AZDEL™ U421B02N (Transverse) | Azdel, Inc. | PP Alloy | AZDEL™ |
| Fainplast PVC KL 101/2 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| DURANEX® 7307 | Polyplastics Co., Ltd. | PC+PBT | DURANEX® |
| 3M™ Dyneon™ Fluoroelastomer MIP 8640X | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |