ASTALON™ H2000R
| Category: | PC , Polycarbonate |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kAOCV4_ASTALON-H2000R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTALON™ H2000R / H2001R / H2003R are low/medium viscosity (high melt flow) grades in the ASTALON™ range and are well suited to difficult to fill injection moulding applications which require a mould release agent (R). Offering an excellent balance of transparency, toughness, heat resistance, flame retardancy and processability, typical applications include security cases and point of sale displays. Note: [ Standard grade = H2000R ] / [ FDA approved = H2001R ] / [ Steam resistant = H2003R ]. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 22 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.24 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 61.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 120 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 2350 | MPa | ASTM D790 |
| Flexural Strength 4(6.40 mm) | 88.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 580 | J/m | ASTM D256 |
| Gardner Impact (3.20 mm) | 75.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 141 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 131 | °C | |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.1E+16 | ohms·cm | ASTM D257 |
| Dielectric Constant | 2.85 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (Total, 3000 µm) | 85.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 125 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Rear Temperature | 230 to 245 | °C | |
| Middle Temperature | 240 to 255 | °C | |
| Front Temperature | 250 to 265 | °C | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 110 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 4.0 to 8.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 20 mm/min |
| 2 . | 20 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3281 | RTP Company | ETFE | RTP |
| SUSTAVACU 6 GF | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAVACU |
| Niche PPCM10BK | Niche Polymer, LLC | PP Copolymer | Niche |
| Andur M-22 (TEG) | Anderson Development Company | PUR-Ester/MDI | Andur |
| LNP™ VERTON™ RV008ES compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |