BJB Polyurethane TC-865 A/B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kAN5Rg_BJB-Polyurethane-TC-865-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TC-865 A/B is medium viscosity, economical and easy to handle two component urethane compound. This system cures relatively fast at room temperature producing tough, impact resistant casting. TC-865 A/B is recommended in applications where a resilient surface hardness is desired while maintaining good flexibility. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 1.13 | g/cm³ | ASTM D792 |
| -- | 1.15 | g/cm³ | ASTM D792 |
| -- 2 | 1.18 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow 3(12.7 mm) | 0.50 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 - 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 683 | MPa | ASTM D638 |
| Tensile Strength | 17.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 70 | % | ASTM D638 |
| Flexural Modulus | 640 | MPa | ASTM D790 |
| Flexural Strength | 19.8 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 102 | kN/m | ASTM D624 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 45 | J/m | ASTM D256 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Component a | Mixing ratio by weight: 100, mixing ratio by capacity: 100 | ||
| Component B | Mixing ratio by weight: 100, mixing ratio by capacity: 95 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | Internal method | ||
| 25°C 4 | 1500 | cP | Internal method |
| 25°C 5 | 1350 | cP | Internal method |
| 25°C | 1400 | cP | Internal method |
| Demold Time (25°C) | > 180 | min | |
| Post Cure Time (71°C) | 16 | hr | |
| Work Time | 10.0 | min |
| Additional Information |
|---|
| Cure schedule:Most of the physical properties can be achieved in 5-7 days at ambient temperature, 77°F (25°C). In order to achieve maximum physical properties, a post cure with heat is required. BJB recommends 24 hours at ambient temperature, 77°F (25°C), followed by 16 hours at 160°F (71°C). |
| Note Message | |
|---|---|
| 1 . | Part A |
| 2 . | Part B |
| 3 . | 12 x 0.5 x 0.5 in |
| 4 . | Part B |
| 5 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 136 | RTP Company | PP, Unspecified | RTP |
| Shinblend® A724 | Shinkong Synthetic Fiber Corp. | PC+PBT | Shinblend® |
| Adiprene® LF 751D | Chemtura | PUR-Ether/TDI | Adiprene® |
| Fainplast PVC PK 71/FR | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Karina CLEAR PVC COMPOUND 80/229-IS-RG-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |