MAJ'ECO EP379HGM - 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJ'ECO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | kAGwF6_MAJ-ECO-EP379HGM---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJ'ECO EP379HGM - 8229 is a vegetal fibre reinforced polypropylene compound intended for injection moulding. MAJ'ECO EP379HGM - 8229 has been developed especially for demanding applications in various engineering sectors. APPLICATIONS Product such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.60 - 1.1 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 42.0 | MPa | ISO 527-2/50 |
| Flexural Modulus 1 | 3250 | MPa | ISO 178 |
| Flexural Stress | 76.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.3 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 24 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 159 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 127 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 150 - 190 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® A1400 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| Sinvicomp SRF3711 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| IPC PP 4840H-C | International Polymers Corporation | PP Homopolymer | IPC PP |
| Pearlbond™ 103 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |
| LNP™ STAT-KON™ RFD03 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |