LNP™ THERMOCOMP™ RF00AH compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k9II7k_LNPTHERMOCOMPRF00AHcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RF00AH is a compound based on Nylon 66 resin containing Glass Fiber. Also known as: LNP* THERMOCOMP* Compound RF-100-10 Product reorder name: RF00AH |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.60 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.30 - 0.50 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.1 - 1.3 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.2 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.37 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.40 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 17200 | MPa | ASTM D638 |
| -- | 17800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 166 | MPa | ASTM D638 |
| Fracture | 182 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 7.8 | % | ASTM D638 |
| Fracture | 8.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 14500 | MPa | ASTM D790 |
| -- | 14900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 262 | MPa | ASTM D790 |
| -- | 265 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 2 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 940 | J/m | ASTM D4812 |
| 23°C 3 | 60 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 253 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 244 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 243 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 5.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 5.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 2.2E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BR13BK6544 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| TOTAL Polyethylene HDPE 9260 | TOTAL Refining & Chemicals | HDPE, MMW | TOTAL Polyethylene |
| Alkathene® XLF197 | Qenos Pty Ltd | LLDPE | Alkathene® |
| PLUSTEK RA320G6 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| Sylvin 8878-80 White 1300 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |