Order Products : sales@su-jiao.com
NORYL™ GFN1F resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k8ggOO_NORYLGFN1Fresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPE+PS blend. 10% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolytic stability. Dimensional stability. Suitable for fluid engineering applications including water filter and water meter components. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 4.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 4.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.55 - 0.66 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.12 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4400 | MPa | ASTM D638 |
| -- | 3900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 75.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 75.0 | MPa | ASTM D638 |
| Fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 3.5 | % | ASTM D638 |
| Yield | 4.5 | % | ISO 527-2/50 |
| Fracture 5 | 3.5 | % | ASTM D638 |
| Fracture | 4.5 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 3400 | MPa | ASTM D790 |
| -- 7 | 3700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 115 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 105 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 80 | J/m | ASTM D256 |
| 23°C | 84 | J/m | ASTM D256 |
| -30°C 10 | 9.0 | kJ/m² | ISO 180/1A |
| 23°C 11 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 410 | J/m | ASTM D4812 |
| -30°C 12 | 30 | kJ/m² | ISO 180/1U |
| 23°C 13 | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 20.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 135 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 130 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 14 | 129 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 138 | °C | ASTM D1525, ISO 306/B50 10 15 |
| -- | 140 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 4.5E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 3.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 8.2E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 260 - 304 | °C | |
| Middle Temperature | 271 - 310 | °C | |
| Front Temperature | 282 - 316 | °C | |
| Nozzle Temperature | 293 - 316 | °C | |
| Processing (Melt) Temp | 293 - 316 | °C | |
| Mold Temperature | 76.7 - 104 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 mm |
| 15 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TufCoat™ IDES 208539 | Lucite International Inc. | Acrylic (PMMA) | TufCoat™ |
| ADDINYL C2 ZV30 | ADDIPLAST | Nylon 66/6 | ADDINYL |
| Daelim Po1y® PP-124 | DAELIM INDUSTRIAL CO., LTD. | PP, Unspecified | Daelim Po1y® |
| EnCom GF10 PC | EnCom, Inc. | PC | EnCom |
| PLASTRON™ PA6-GF60-01 | Daicel Polymer Ltd. | Nylon 6 | PLASTRON™ |