SEPAZ™ LB30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | SEPAZ™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k8TmYo_SEPAZ-LB30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SEPAZ™ LB30 is a Polyamide 6 (Nylon 6) product filled with 30% long glass fiber. It is available in Asia Pacific. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow | 0.30 | % | |
| Across Flow | 0.40 | % | |
| Water Absorption (24 hr) | 1.2 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 162 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 8340 | MPa | ASTM D790 |
| Flexural Strength | 240 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 240 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 215 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60°C Mold Temperature |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 285 FR | RTP Company | Nylon 66 | RTP |
| SATRAN® ABS 805 | MRC Polymers, Inc. | ABS | SATRAN® ABS |
| Arnite® A06 700 | DSM Engineering Plastics | PET | Arnite® |
| EZPrene 9080A | ENPLAST Americas, a Ravago Group Company | TPV | EZPrene |
| MAJORIS AFR961 - 8229 | AD majoris | PP Copolymer | MAJORIS |