HIDEN® P502 YE
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | YUHWA Korea Petrochemical Ind. Co., Ltd. |
| Trademark: | HIDEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k8I9Ot_HIDEN-P502-YE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HIDEN® P502 YE is a High Density Polyethylene material. It is available in Asia Pacific. Important attributes of HIDEN® P502 YE are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.941 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.15 | g/10 min | ASTM D1238 |
| Water Absorption (Equilibrium) | < 0.010 | % | ASTM D570 |
| Environmental Stress-Cracking Resistance 1(Condition B) | > 5000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 58 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 19.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 600 | % | ASTM D638 |
| Flexural Modulus | 588 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | > 490 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 57.0 | °C | ASTM D648 |
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 120 | °C | ASTM D1525 |
| Peak Melting Temperature | 130 | °C | ASTM D3418 |
| CLTE - Flow | 1.5E-4 | cm/cm/°C | ASTM D696 |
| Oxidation Induction Time (200°C) | > 40 | min |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Pigment Dispersion | < 3.00 | ISO 18553 |
| Note Message | |
|---|---|
| 1 . | 100% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 8854 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| Braskem PE TX7003 | Braskem | LDPE | Braskem PE |
| Evermore PUR UP-6042NR | Evermore Chemical Industry Co., Ltd. | PUR-Ester | Evermore PUR |
| KOPLA PA66 KDG1030 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |
| SCHULABLEND® (ASA/PA) M/MW 6201 MT | A. Schulman Europe | ASA+Nylon | SCHULABLEND® |