Radilon® A CV300 333 NER
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k7te2D_Radilon-A-CV300-333-NER.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 30% glass beads filled injection moulding grade. Black colour. Suitable for parts requiring low warpage and good surface aspect. ISO 1043 : PA66 GB30 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.34 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 7.6 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.7 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4300 | 2700 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 77.0 | 40.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 7.0 | 10 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 3700 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 125 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 | 28 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 200 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 225 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 260 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shuman PC SP910 | Shuman Plastics, Inc. | PC | Shuman PC |
| Axiall PVC 3801 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Hanwha Total PP RF402 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Hifax TKC 243P Black | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| LNP™ LUBRICOMP™ UFL36AS compound | SABIC Innovative Plastics | PPA | LNP™ LUBRICOMP™ |