Durethan® AKV 30 XTS1 901510
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k7qip5_DurethanAKV30XTS1901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 30% glass fibers, injection molding, heat-aging stabilized, notably high heat-aging stability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Vertical flow direction : 290°C, 2.00mm 1 | 1.0 | -- | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.050 | -- | % | ISO 2577 |
| Flow direction : 290°C, 2.00mm 3 | 0.37 | -- | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.070 | -- | % | ISO 2577 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 9900 | 6000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 175 | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | 5.5 | % | ISO 527-2/5 |
| Nominal Tensile Strain at Break (23°C) | 4.2 | 5.7 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 9000 | 5800 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% strain, 23°C | 260 | 150 | MPa | ISO 178/A |
| 23°C 6 | 270 | 180 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 4.0 | 5.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | ISO 1874 - PA 66, GHR, 14-100, GF30 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 - 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 8.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 9.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 65 | -- | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 8.0 | -- | kJ/m² | ISO 180/1A |
| 23°C | 10 | -- | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 50 | 80 | kJ/m² | ISO 180/1U |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 235 | -- | °C | ISO 75-2/A |
| Melting Temperature 8 | 263 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C | 2.5E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 9.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 - 6.0 | hr | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sipolprene® 63210 B | SIPOL S.p.A | TPC-ET | Sipolprene® |
| Nanguang TPU S-95AX | Fujian Nanguang Light Industry Co., Ltd. | TPU, Unspecified | Nanguang TPU |
| Niretan A F20 AE/V2 | Soredi S.p.a. | Nylon 66 | Niretan A |
| CP PRYME® PC/ABS PCA300 | Chase Plastics Services Inc. | PC+ABS | CP PRYME® PC/ABS |
| EchoShield 1114X5 | DN Plastics | TPO (POE) | EchoShield |