Kinta NB3610G
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Kinta Technology (Hong Kong) Co., Ltd. |
| Trademark: | Kinta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k7QMwR_KintaNB3610G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Kinta NB3610G is an acrylonitrile butadiene styrene (ABS) product, which contains a 10% glass fiber reinforced material. It is available in the Asia-Pacific region. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.30 - 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 67.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 10 | % | ASTM D638 |
| Flexural Modulus 3 | 3800 | MPa | ASTM D790 |
| Flexural Strength 4 | 112 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 10.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 97.0 | °C | ASTM D648 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 44 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.2 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75 - 80 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 200 - 205 | °C | |
| Middle Temperature | 205 - 210 | °C | |
| Front Temperature | 200 - 205 | °C | |
| Nozzle Temperature | 210 - 220 | °C | |
| Processing (Melt) Temp | 205 - 210 | °C | |
| Mold Temperature | 80 - 90 | °C | |
| Injection Pressure | 100 - 130 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VERSIFY™ 3401 | The Dow Chemical Company | TPO (POE) | VERSIFY™ |
| CGPC PVC SO-30X (70 phr Plasticizer C) | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| Geon™ Vinyl Rigid Extrusion 87717 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Karina CLEAR PVC COMPOUND -E 80/311-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PERLER® N09H2500B11 | A.D. Compound S.p.A. | PP Copolymer | PERLER® |