Formolene® HL3812
| Category: | MDPE , Medium Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation, U.S.A. |
| Trademark: | Formolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k6isId_Formolene-HL3812.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Formolene® HL3812 is a high molecular weight hexene copolymer resin that is tailored specifically for geomembrane applications. The resin provides an excellent balance of ESCR properties, broad fusion range, excellent melt strength and good overall processability. Suggested Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.938 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.080 | g/10 min | |
| 190°C/21.6 kg | 12 | g/10 min | |
| Environmental Stress-Cracking Resistance | |||
| 10% Igepal, F50 | > 1500 | hr | ASTM D1693B |
| 100% Igepal, F50 | > 1500 | hr | ASTM D1693C |
| SP-NCTL | > 1.4 | month | ASTM D5397 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 17.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 850 | % | ASTM D638 |
| Flexural Modulus - Tangent 3(Compression Molded) | 827 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 4 | 504 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 58.9 | °C | ASTM D648 |
| Brittleness Temperature | < -75.0 | °C | ASTM D746A |
| Vicat Softening Temperature | 47.2 | °C | ASTM D1525 5 |
| Note Message | |
|---|---|
| 1 . | Type IV, 51 mm/min |
| 2 . | Type IV, 51 mm/min |
| 3 . | 13 mm/min |
| 4 . | Type S |
| 5 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BESHV | Arkema | Nylon 11 | Rilsan® |
| Styromer e-S0799 | Inverko Compounding B.V. | PS (GPPS) | Styromer |
| 3M™ Dyneon™ TFM™ Modified PTFE TFM 2070Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE |
| Karina GRAY PVC COMPOUND 105950-18/365-A-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PALSTYROL® R S 12 | pal plast GmbH | PS (GPPS) | PALSTYROL® |