Jackdaw PC DR15NT6341
| Category: | PC , Polycarbonate |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | Jackdaw PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k6f99M_Jackdaw-PC-DR15NT6341.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jackdaw PC DR15NT6341 is a Polycarbonate (PC) product filled with 25% glass fiber. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 0.20 to 0.50 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.24 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 110 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 6500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 135 | MPa | ISO 178 |
| Break | 135 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 12 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 150 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 140 | °C | ASTM D648, ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V72G | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| PrimoFlo 30A-300 | KMI Group Inc. | SEBS | PrimoFlo |
| TPUCO® TPUI-G95 | Taiwan PU Corporation | TPU-Capro | TPUCO® |
| HI-ZEX™ 6203B | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| Petrothene® M2612GU | LyondellBasell Industries | LDPE | Petrothene® |