Generic Nylon 9T - Glass Fiber
| Category: | Nylon 9T , Polyamide 9T |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k6FrU4_Generic-Nylon-9T---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 9T - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 to 1.73 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (320°C/2.16 kg) | 15 to 17 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.098 to 0.20 | % | ASTM D955 |
| Across Flow : 23°C | 0.50 to 0.80 | % | ASTM D955 |
| 23°C | 0.20 to 0.90 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 165 to 181 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 9960 to 13100 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 197 to 270 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 to 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 285 to 290 | °C | ASTM D648 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (23°C) | 3.30 to 3.80 | ASTM D150 | |
| Dissipation Factor (23°C) | 9.0E-3 to 0.010 | ASTM D150 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3502 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| MTEGRITY™ ABS AB305 | M. Holland Company | ABS | MTEGRITY™ ABS |
| Varcum 29557 | Durez Corporation | Phenolic | Varcum |
| Ecodear® Prototype - High PLA Content | Toray Resin Company | PLA | Ecodear® |
| Edgetek™ X ET3300-8031 NHFR NC001 | PolyOne Corporation | PBT | Edgetek™ |