TECHNYL® C 206F NATURAL (R)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k5olvn_TECHNYLC206FNATURALR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECHNYL® C 206F Natural (R) is an unreinforced polyamide PA6, standard for fast injection cycles, for injection moulding. This grade has high fluidity and a good mould release. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 0.35 | -- | % | ISO 294-4 |
| Flow | 0.65 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.3 | -- | % | ISO 62 |
| Saturated, 23°C | 2.7 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.6 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | 1100 | MPa | ISO 527-2/1A |
| Tensile Stress | ISO 527-2/1A | |||
| Yield, 23°C | 85.0 | 45.0 | MPa | ISO 527-2/1A |
| Fracture, 23°C | 50.0 | 60.0 | MPa | ISO 527-2/1A |
| Tensile Strain | ISO 527-2 | |||
| Yield, 23°C | 4.0 | 30 | % | ISO 527-2 |
| Fracture, 23°C | 15 | > 200 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2800 | 1000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 100 | 40.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | 88 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact (23°C) | 5.0 | 80 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 60.0 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | -- | 18 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.40 | 3.90 | IEC 60250 | |
| Dissipation Factor | 0.023 | 0.10 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (3.2 mm) | V-2 | -- | UL 94 | |
| Glow Wire Ignition Temperature (0.8 mm) | 675 | -- | °C | IEC 60695-2-13 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 - 235 | °C | |
| Middle Temperature | 235 - 240 | °C | |
| Front Temperature | 235 - 245 | °C | |
| Mold Temperature | 60 - 80 | °C |
| Injection instructions |
|---|
| The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For unfilled polyamide, Solvay recommends the use of high alloy steel with a weak chromium content. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinite® PET T101G45 | Shinkong Synthetic Fiber Corp. | PET | Shinite® PET |
| Sevrene® 3068-65A-0000 | Vi-Chem Corporation | TPE | Sevrene® |
| Silopren® LSR 4630FC | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| LNP™ LUBRICOMP™ KP004XXP compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |
| WELLAMID Nylon 6000 MRCF 15/15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |