LNP™ THERMOCOMP™ JF004P compound
| Category: | PESU , Polyethersulfone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k5QWqF_LNP-THERMOCOMP-JF004P-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP JF004P is a compound based on Polyethersulfone resin containing 20% Glass Fiber. Added features of this material include: Exceptional Processing. Also known as: LNP* THERMOCOMP* Compound JF-1004 EP Product reorder name: JF004P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage - Flow (24 hr) | 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 7610 | MPa | ASTM D638 |
| Tensile Strength (Break) | 120 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638 |
| Flexural Modulus | 7410 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 500 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 207 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 360 to 371 | °C | |
| Front Temperature | 371 to 382 | °C | |
| Processing (Melt) Temp | 354 to 371 | °C | |
| Mold Temperature | 138 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HMP-305W (Roto) | Ravago Manufacturing Americas, LLC | LMDPE | Ravago Compounds |
| Starpylen MF004S | Eurostar Engineering Plastics | PP, Unspecified | Starpylen |
| VENELENE® 3200B | Poliolefinas Internacionales, C.A. (Polinter) | HDPE | VENELENE® |
| BMC HT12-1024 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| LNP™ LUBRICOMP™ RFL36 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ LUBRICOMP™ |