LNP™ LUBRICOMP™ SCP36 compound
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k4gwsA_LNP-LUBRICOMP-SCP36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP SCP36 is a compound based on Nylon 12 containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this grade include: Wear Resistant, Electrically Conductive. Also known as: LNP* LUBRICOMP* Compound SCL-4536 Product reorder name: SCP36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 | % | |
| Across Flow : 24 hr | 0.50 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.16 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.24 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 1 | 1.00 | MPa | ASTM D638 |
| Break | 122 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 2 | 1.0 | % | ASTM D638 |
| Break | 1.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 3 | 16200 | MPa | ASTM D790 |
| -- 4 | 16000 | MPa | ISO 178 |
| Flexural Strength 5(Break, 50.0 mm Span) | 178 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.47 | ||
| vs. Itself - Static | 0.33 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.00 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 14.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 82 | J/m | ASTM D256 |
| 23°C 6 | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 510 | J/m | ASTM D4812 |
| 23°C 7 | 34 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 10.0 | J | ASTM D3763 |
| -- | 2.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 178 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 8 | 177 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 173 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 169 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.2E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.1E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 105 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40.0 to 60.0 | °C | |
| Rear Temperature | 240 to 260 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Nozzle Temperature | 250 to 270 | °C | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 60.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MBA PP 2117 | MBA Polymers | PP Copolymer | MBA PP |
| Abstron HI40B | Bhansali Engineering Polymers Limited | ABS | Abstron |
| China PPS hMR60 | Sichuan Deyang Chemical Co., Ltd | PPS | China PPS |
| Hostacom DKC 179N | LyondellBasell Industries | PP Alloy | Hostacom |
| Kepital® TE-23S | KEP Americas | Acetal (POM) Copolymer | Kepital® |