VICTREX® PEEK 150GL30 BLACK
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Victrex plc |
| Trademark: | VICTREX® PEEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k4I4g0_VICTREX-PEEK-150GL30-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High performance thermoplastic material, 30% glass fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding, easy flow, FDA food contact compliant, colour black. Complex geometries with thin cross sections or long flow lengths where higher strength in a static system is required. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilization for medical and food contact applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.52 | g/cm³ | ISO 1183 |
| Spiral Flow 2 | 15.0 | cm | Internal method |
| Molding Shrinkage 3 | ISO 294-4 | ||
| Vertical flow direction : 180°C | 0.90 | % | ISO 294-4 |
| Flow direction : 180°C | 0.30 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.20 mm | 0.040 | % | ISO 62 |
| Balance, 23°C, 3.20mm, 50% RH | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 87 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 12000 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, 23°C | 190 | MPa | ISO 527-2 |
| Fracture, 125°C | 115 | MPa | ISO 527-2 |
| Fracture, 175°C | 70.0 | MPa | ISO 527-2 |
| Fracture, 225°C | 55.0 | MPa | ISO 527-2 |
| Fracture, 275°C | 40.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.4 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 11500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 270 | MPa | ISO 178 |
| Compressive Stress | ISO 604 | ||
| 23°C | 250 | MPa | ISO 604 |
| 120°C | 160 | MPa | ISO 604 |
| 200°C | 55.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 7.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | 50 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 335 | °C | ISO 75-2/A |
| Glass Transition Temperature | 143 | °C | ISO 11357-2 |
| Melting Temperature | 343 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : > 143°C | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : < 143°C | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : < 143°C | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : > 143°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1700 | J/kg/°C | DSC |
| Thermal Conductivity (23°C) | 0.30 | W/m/K | ISO 22007-4 |
| RTI Elec | 240 | °C | UL 746 |
| RTI Imp | 220 | °C | UL 746 |
| RTI | 240 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 22 | kV/mm | IEC 60243-1 |
| Dielectric Constant (23°C, 1 kHz) | 3.40 | IEC 60250 | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C) | 290 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Hopper Temperature | < 100 | °C | |
| Rear Temperature | 360 | °C | |
| Middle Temperature | 365 - 370 | °C | |
| Front Temperature | 375 | °C | |
| Nozzle Temperature | 380 | °C | |
| Mold Temperature | 170 - 200 | °C |
| Injection instructions |
|---|
| Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness |
| Note Message | |
|---|---|
| 1 . | Crystalline |
| 2 . | Mold temperature: 180°C, melt temperature: 380°C |
| 3 . | 380°C nozzle |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 9035 | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| TPV Elastoprene® N40D-S | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| Dryflex® 422501S | ELASTO | SBS | Dryflex® |
| HiFill® PP 0114 TC-1 | Techmer Engineered Solutions | PP, Unspecified | HiFill® |
| LNP™ STAT-KON™ DEL36 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |