LNP™ LUBRICOMP™ OCL36 compound
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k3v9bt_LNPLUBRICOMPOCL36compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Lubricomp* OCL36 is a compound based on PPS - Linear resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive. Also known as: LNP* LUBRICOMP* Compound OCL4036L Product reorder name: OCL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (315°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 24 hours | 0.35 - 0.40 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.050 - 0.10 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 24900 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 163 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.80 | % | ISO 527-2 |
| Flexural Modulus | 21300 | MPa | ISO 178 |
| Flexural Stress | 219 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.39 | ASTM D3702 Modified | |
| With Self-Static | 0.34 | ASTM D3702 Modified | |
| Wear Factor - Washer | 19.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 2(23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3 | |||
| 0.45 MPa, unannealed, 64.0mm span | 258 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 278 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 5.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 - 1.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 - 316 | °C | |
| Middle Temperature | 321 - 332 | °C | |
| Front Temperature | 332 - 343 | °C | |
| Processing (Melt) Temp | 316 - 321 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Addisil™ 6300 | Momentive Performance Materials Inc. | Silicone | Addisil™ |
| Baoding 6185B | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU, Unspecified | Baoding |
| Cosmic Epoxy EH21 | Cosmic Plastics, Inc. | Epoxy | Cosmic Epoxy |
| ENVIROPLAS® ENV17-NC060 | ENVIROPLAS®, Inc. | PEI | ENVIROPLAS® |
| Plaslube® PA6/6 M/TL7 HS L | Techmer Engineered Solutions | Nylon 66 | Plaslube® |