Category: | PP Homopolymer , Polypropylene Homopolymer |
Manufacturer: | Braskem America Inc. |
Trademark: | Braskem PP |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | k3Hc6X_Braskem-PP-D180A2.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Sub-group Homopolymer Description Excellent melt stability Applications Suggested uses include BCF mulit-filaments, high tenacity continuous filament yarn, fine denier staple fibers |
General Information | |
---|---|
Features |
|
Uses |
|
Agency Ratings |
|
Forms |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ASTM D1238 |
Hardness | Nominal Value | Unit | Test Method |
---|---|---|---|
Rockwell Hardness (R-Scale, Injection Molded) | 104 | ASTM D785 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Strength 1(Yield, Injection Molded) | 35.2 | MPa | ASTM D638 |
Tensile Elongation 2(Yield, Injection Molded) | 9.0 | % | ASTM D638 |
Flexural Modulus - 1% Secant 3(Injection Molded) | 1520 | MPa | ASTM D790A |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact (23°C, Injection Molded) | 37 | J/m | ASTM D256A |
Additional Information | Nominal Value | Unit | Test Method |
---|---|---|---|
Elongation of Fibers 4 | 93 | % | ASTM D2256 |
Takeup Roll Speed | 33.3 | m/sec | Internal Method |
Tenacity of Fibers 5 | 2.90 | g/denier | ASTM D2256 |
Note Message | |
---|---|
1 . | 51 mm/min |
2 . | 51 mm/min |
3 . | 1.3 mm/min |
4 . | 3.3 draw ratio, 1,250 m/min roll speed, 225°C spin temperature, D1000/68 |
5 . | 3.3 draw ratio, 1,250 m/min roll speed, 225°C spin temperature, D1000/68 |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Niblan V100 AE V0/M | Soredi S.p.a. | PBT | Niblan |
GETILAN ATP/190 X1 3A | Crosspolimeri S.p.A. | XLPE | GETILAN |
Hifax TRC 135X/4 BLACK | LyondellBasell Industries | PP Copolymer | Hifax |
Lupoy® GP1000MU | LG Chem Ltd. | PC | Lupoy® |
Hostalen PP H2992 | LyondellBasell Industries | PP Impact Copolymer | Hostalen |