NANCAR® 1072
| Category: | NBR , Acrylonitrile Butadiene Rubber |
| Manufacturer: | Nantex Industry Co., Ltd. |
| Trademark: | NANCAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k2EokU_NANCAR-1072.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NANCAR® 1072 is a carboxyl-modified nitrile rubber with medium-high oil resistance. It may be processed like normal nitrile rubber except that metal oxide is added at the end of the mixing cycle. NANCAR® 1072 offers outstanding abrasion and wear resistance. It is recommended for use in belts, industrial rollers, wheels, shoe soles, heels and other mechanical goods requiring high abrasion resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.980 | g/cm³ | |
| Mooney Viscosity (ML 1+4, 100°C) | 48 | MU | ASTM D1646 |
| Acrylonitrile Content - Bound | 26.5 | % | Internal Method |
| Stabilizer | Non-staining |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion - Test, c.c 1 | 53 | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Loss | 0.40 | % | ASTM D5688 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Abrasion Index - NBS test | 911 | ASTM D1630 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 2(Shore A) | 80 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3(300% Strain) | 15.7 | MPa | ASTM D412 |
| Tensile Strength 4(Yield) | 25.0 | MPa | ASTM D412 |
| Tensile Elongation 5(Break) | 460 | % | ASTM D412 |
| Tear Strength | 53.9 | kN/m | ASTM D624 |
| Compression Set 6(100°C, 70 hr) | 57 | % | ASTM D395 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 7(100°C, 70 hr) | 7.0 | % | ASTM D865 |
| Change in Ultimate Elongation in Air 8(100°C, 70 hr) | -26 | % | ASTM D865 |
| Change in Durometer Hardness in Air 9(Shore A, 100°C, 70 hr) | 5.0 | ASTM D865 | |
| Change in Tensile Strength 10 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM #1 Oil | 9.0 | % | |
| 100°C, 70 hr, in ASTM #3 Oil | -14 | % | |
| Change in Ultimate Elongation 11 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM #1 Oil | -28 | % | |
| 100°C, 70 hr, in ASTM #3 Oil | -20 | % | |
| Change in Durometer Hardness 12 | ASTM D471 | ||
| Shore A, 100°C, 70 hr, in ASTM #1 Oil | 7.0 | ||
| Shore A, 100°C, 70 hr, in ASTM #3 Oil | -6.0 | ||
| Change in Volume 13 | ASTM D471 | ||
| 100°C, 70 hr, in ASTM Oil #1 | -4.6 | % | |
| 100°C, 70 hr, in ASTM Oil #3 | 14 | % |
| Note Message | |
|---|---|
| 1 . | (Load weight: 10 NT) |
| 2 . | Cured for 15.0 min at 160°C |
| 3 . | Cured for 15.0 min at 160°C |
| 4 . | Cured for 15.0 min at 160°C |
| 5 . | Cured for 15.0 min at 160°C |
| 6 . | Cured for 15.0 min at 160°C |
| 7 . | Cured for 15.0 min at 160°C |
| 8 . | Cured for 15.0 min at 160°C |
| 9 . | Cured for 15.0 min at 160°C |
| 10 . | Cured for 15.0 min at 160°C |
| 11 . | Cured for 15.0 min at 160°C |
| 12 . | Cured for 15.0 min at 160°C |
| 13 . | Cured for 15.0 min at 160°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3582 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Hifax CA 10 A | LyondellBasell Industries | TPO (POE) | Hifax |
| Latigray 82-03 CW/95 | LATI S.p.A. | Nylon 12 | Latigray |
| Sylvin 8240-80FU Brown 7425 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ SF00A compound | SABIC Innovative Plastics | Nylon 12 | LNP™ THERMOCOMP™ |