DOW™ LDPE 150E
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k1ESKT_DOW-LDPE-150E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOW LDPE™150E low density polyethylene resin can be extruded by ordinary blown film process, and the melt temperature is between 170 and 230°C. The properly prepared DOW LDPE 150E low density polyethylene resin integrates processability, stiffness and physical properties. Remarks: DOW LDPE 150E low density polyethylene should meet the following regulatory requirements: EU, no 10/2011 us food and drug administration regulations 21 CFR 177.1520(c)2.2 us food and drug administration regulations-drug master document (DMF) please inquire regulations for complete details application fields:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.921 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 100 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| 2% secant, MD : 100 µm | 128 | MPa | ISO 527-3 |
| 2% secant, TD : 100 µm | 128 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 100 µm | 9.20 | MPa | ISO 527-3 |
| TD : Yield, 100 µm | 7.60 | MPa | ISO 527-3 |
| MD : Break, 100 µm | 21.0 | MPa | ISO 527-3 |
| TD : Break, 100 µm | 20.5 | MPa | ISO 527-3 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 100 µm | 470 | % | ASTM D882 |
| TD : Break, 100 µm | 530 | % | ASTM D882 |
| Dart Drop Impact (100 µm) | 430 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 100 µm | 270 | g | ASTM D1922 |
| TD : 100 µm | 480 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ASTM D1525 |
| Extrusion instructions |
|---|
| 放大比 1:2.5 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mediprene® OF 701M | ELASTO | TPE | Mediprene® |
| Jackdaw Nylon XI10NT6643 | Jackdaw Polymers | Nylon+PP | Jackdaw Nylon |
| Pacrel® 5365N-EA | Nanjing Jinling OPTA Polymer Co., Ltd. | TPE | Pacrel® |
| ESTOPLAST SR 1500NN01 | Ester Industries Ltd. | ABS | ESTOPLAST SR |
| LNP™ STAT-KON™ DEL329XF compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |