LNP™ STAT-KON™ DE004 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | k0TIxZ_LNPSTATKONDE004compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* DE004 is a compound based on Polycarbonate resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound DC-1004 Product reorder name: DE004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.040 - 0.10 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.30 - 0.40 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.37 - 0.45 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.040 - 0.090 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.15 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.22 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10900 | MPa | ASTM D638 |
| -- | 10600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 121 | MPa | ASTM D638 |
| Fracture | 114 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.2 | % | ASTM D638 |
| Fracture | 1.6 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9790 | MPa | ASTM D790 |
| -- | 9780 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 196 | MPa | ASTM D790 |
| -- | 188 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 73 | J/m | ASTM D256 |
| 23°C 2 | 6.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 490 | J/m | ASTM D4812 |
| 23°C 3 | 33 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 15.6 | J | ASTM D3763 |
| -- | 3.41 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 147 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 149 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 144 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 144 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 1.4E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 4.2E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 4.3E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 10 - 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnoform® 300 GB6 | Grupa Azoty S.A. | Acetal (POM) Copolymer | Tarnoform® |
| VESTAMID® Care ME47 | Evonik Industries AG | PEBA-Ether | VESTAMID® Care |
| ALCOM® POM 770/1.1 CF20 | ALBIS PLASTIC GmbH | Acetal (POM) Copolymer | ALCOM® POM |
| Europrene® N 3345 GRN | Versalis S.p.A. | NBR | Europrene® |
| Fiberfil® J-60/30/E | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |