LNP™ STAT-LOY™ AF306 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | izTW5a_LNP-STAT-LOY-AF306-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Stat-loy* AF306 is a compound based on Acrylonitrile Butadiene Styrene resin containing Glass Fiber. Added features of this material include: Antistat. Also known as: LNP* STAT-LOY* Compound AF-30 Product reorder name: AF306 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.29 | g/cm³ | ASTM D792 |
| -- | 1.28 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 to 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.45 | % | ISO 294-4 |
| Flow : 24 hr | 0.30 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 3.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6890 | MPa | ASTM D638 |
| -- | 6010 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 38.6 | MPa | ASTM D638 |
| Yield | 43.0 | MPa | ISO 527-2 |
| Break | 38.6 | MPa | ASTM D638 |
| Break | 43.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 1.0 | % | ASTM D638 |
| Yield | 1.1 | % | ISO 527-2 |
| Break | 1.0 | % | ASTM D638 |
| Break | 1.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5520 | MPa | ASTM D790 |
| -- | 5700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 48.3 | MPa | ASTM D790 |
| -- | 63.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 2 | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 250 | J/m | ASTM D4812 |
| 23°C 3 | 17 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.90 | J | ASTM D3763 |
| -- | 1.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 102 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 103 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 95.6 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 71.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 4.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+10 to 1.0E+12 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 204 to 216 | °C | |
| Processing (Melt) Temp | 199 to 210 | °C | |
| Mold Temperature | 10.0 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 103 CC HI | RTP Company | PP, Unspecified | RTP |
| KOPELEN JH-330M | Lotte Chemical Corporation | PP Impact Copolymer | KOPELEN |
| Karina WHITE PVC COMPOUND 801-10/ 49-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Dryflex® A2 500350 | ELASTO | SEBS | Dryflex® |
| Sarlink® TPE EE-1185B (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |