Adflex Q 100 F
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | izESLs_Adflex-Q-100-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adflex Q 100 F is a thermoplastic polyolefin, which is mainly used by our customers for the extrusion of blown film. It is also suitable for sheet extrusion. Adflex Q 100 F features very high softness and very low modulus. It does not contain any slip or anti-blocking agents. Adflex Q 100 F is used for the production of soft hygienic film and heavy duty film, as well as for the modification of LDPE or LLDPE to increase mechanical characteristics, puncture resistance, and to allow further downgauging. It can be easily processed on conventional LDPE or LLDPE blown film lines. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.880 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.60 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 30 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 10.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 400 | % | ISO 527-2 |
| Flexural Modulus | 100 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3/25 | ||
| MD : 50 µm, blown film | 90.0 | MPa | ISO 527-3/25 |
| TD : 50 µm, blown film | 90.0 | MPa | ISO 527-3/25 |
| Tensile Stress | ISO 527-3/500 | ||
| MD : Yield, 50 µm, blown film | 7.50 | MPa | ISO 527-3/500 |
| TD : Yield, 50 µm, blown film | 7.50 | MPa | ISO 527-3/500 |
| MD : Broken, 50 µm, blown film | 40.0 | MPa | ISO 527-3/500 |
| TD : Broken, 50 µm, blown film | 37.0 | MPa | ISO 527-3/500 |
| Tensile Elongation | ISO 527-3/500 | ||
| MD : Yield, 50 µm, blown film | 40 | % | ISO 527-3/500 |
| TD : Yield, 50 µm, blown film | 40 | % | ISO 527-3/500 |
| MD : Broken, 50 µm, blown film | 1000 | % | ISO 527-3/500 |
| TD : Broken, 50 µm, blown film | 1000 | % | ISO 527-3/500 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | No Break | ISO 180/1A | |
| 23°C | No Break | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 40.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 60.0 | °C | ISO 306/A50 |
| Melting Temperature | 140 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm) | 9 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | 50 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties obtained on blown film produced with laboratory line under internal standard conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tekuform H13 | TEKUMA Kunststoff GmbH | Acetal (POM) Copolymer | Tekuform |
| ACRYLITE® Sheet Optical MR | Evonik Cyro LLC | Acrylic (PMMA) | ACRYLITE® Sheet |
| ESENTTIA 30R40CD | Polipropileno del Caribe S.A. | PP Random Copolymer | ESENTTIA |
| POFEX 8200EP90F | POLYROCKS CHEMICAL CO., LTD | TPE | POFEX |
| Sylvin 8960-80 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |