LNP™ KONDUIT™ RTF2B compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ KONDUIT™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iyyg2d_LNPKONDUITRTF2Bcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* KONDUIT* RTF2B is a compound based on Nylon 66 resin containing 10% Glass Fiber, 55% Thermal Filler. Added features of this material include: Thermally Conductive. Also known as: LNP* KONDUIT* Compound RTF-212-11 Product reorder name: RTF2B |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.04 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.90 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.5 | % | ASTM D955 |
| Lateral flow : 24 hours | 1.5 | % | ISO 294-4 |
| Traffic : 24 hours | 0.93 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.30 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 13100 | MPa | ASTM D638 |
| -- | 11900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture | 102 | MPa | ASTM D638 |
| Fracture | 95.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 1.4 | % | ASTM D638 |
| Fracture | 1.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 11400 | MPa | ASTM D790 |
| -- | 11300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 183 | MPa | ASTM D790 |
| -- | 174 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 37 | J/m | ASTM D256 |
| 23°C 2 | 4.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 450 | J/m | ASTM D4812 |
| 23°C 3 | 35 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.5 | J | ASTM D3763 |
| -- | 2.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 226 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 216 | °C | ISO 75-2/Af |
| Thermal Conductivity | 1.2 | W/m/K | ASTM E1530 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 93 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NITRIFLEX L-2108 | NITRIFLEX | SBR, Unspecified | NITRIFLEX |
| ACCULOY™ PCS003L | ACLO Compounders Inc. | ASA+PC | ACCULOY™ |
| Evermore PUR UDA-10XT | Evermore Chemical Industry Co., Ltd. | PUR-Ether | Evermore PUR |
| ELASTOSIL® LR 3856/20 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Karina BEIGE PVC COMPOUND 828-08/20-AY-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |