Adflex C 200 F
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ixzgmm_Adflex-C-200-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adflex C 200 F is developed for the central layer of tough, transparent co-extruded cast-film structures. It combines transparency with high softness , a very high toughness even at low temperatures and an excellent compatibility with other polyolefins. It does not contain any slip nor anti-blocking agents. Typical applications of the Adflex C 200 F are co-extruded cast-film for food packaging, hygiene applications, surface protection where the outside layer can be any polyolefin homo or copolymer. For regulatory information please refer to Adflex C 200 F Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 41 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 8.00 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 500 | % | ISO 527-2 |
| Flexural Modulus | 220 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3/25 | ||
| MD : 50 µm, Cast Film | 125 | MPa | |
| TD : 50 µm, Cast Film | 110 | MPa | |
| Tensile Stress | ISO 527-3/500 | ||
| MD : Yield, 50 µm, Cast Film | 8.00 | MPa | |
| TD : Yield, 50 µm, Cast Film | 8.00 | MPa | |
| MD : Break, 50 µm, Cast Film | 30.0 | MPa | |
| TD : Break, 50 µm, Cast Film | 24.0 | MPa | |
| Tensile Elongation | ISO 527-3/500 | ||
| MD : Yield, 50 µm, Cast Film | 26 | % | |
| TD : Yield, 50 µm, Cast Film | 33 | % | |
| MD : Break, 50 µm, Cast Film | 990 | % | |
| TD : Break, 50 µm, Cast Film | 890 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 65 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 50.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 89.0 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Cast Film) | 47 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | 8.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BZM 30 TL | Arkema | Nylon 11 | Rilsan® |
| Moplen EP240T | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Network Polymers Nylon 66 | Network Polymers, Inc. | Nylon 66 | Network Polymers Nylon |
| ALCUDIA® EBA PA-1770 | REPSOL | EBA | ALCUDIA® EBA |
| FERROPAK® TPP40WA07BK | Ferro Corporation | PP, Unspecified | FERROPAK® |