Zytel® HTN 92G35DH2 BK083
| Category: | PPA , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ixNPka_Zytel-HTN-92G35DH2-BK083.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass Reinforced, PPA, High Performance Polyamide with DuPont |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.44 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.20 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12000 | 10000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 200 | 157 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.4 | 2.6 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 10000 | MPa | |
| 1000 hr | -- | 8500 | MPa | |
| Flexural Modulus | 10000 | -- | MPa | ISO 178 |
| Flexural Stress | 272 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 10 | 10 | kJ/m² | |
| 23°C | 10 | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | 45 | kJ/m² | |
| 23°C | 55 | 50 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 283 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 310 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.9E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 1.9E-5 | -- | cm/cm/°C | |
| Transverse | 6.3E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 6.3E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 32 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Note Message | |
|---|---|
| 1 . | First Heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACRYPET® IR H70 | Mitsubishi Rayon Co., Ltd. | Acrylic (PMMA) | ACRYPET® |
| ANYBES Nylon 12 Fine Powder | SH Energy & Chemical | Nylon 12 | ANYBES |
| Exxtral™ Performance Polyolefin HMU208 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| HiFill® PEEK CF40 HF | Techmer Engineered Solutions | PEEK | HiFill® |
| Sylvin 5143-88 White 1318 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |