Adell PS IF-10
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Adell Plastics, Inc. |
| Trademark: | Adell PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ix086G_Adell-PS-IF-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adell PS IF-10 is a High Impact Polystyrene material. It is available in North America. Important attributes of Adell PS IF-10 are:
|
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.050 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 65 | ||
| R-Scale | 94 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 26.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 2000 | MPa | ASTM D790 |
| Flexural Strength | 32.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 93.3 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ULTEM™ 2212R resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Abistir® UG AS-UV BIANCO 0301 | SO.F.TER. SPA | ABS | Abistir® |
| Nypol® PA A3 G23 HS NTLA013 NR423 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| BJB Polyurethane TC-885 FR REV 1 | BJB Enterprises, Inc. | PUR, Unspecified | BJB Polyurethane |
| MAJORIS G500 | AD majoris | PP, Unspecified | MAJORIS |