SAXAMID™ 136Q32
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SAX Polymers |
| Trademark: | SAXAMID™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ivNeRx_SAXAMID-136Q32.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SAXAMID 136Q32 is a high impact-modified polyamide 6 injection-molding-grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 150 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 56.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 10 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1800 | MPa | ISO 178 |
| Flexural Stress 2 | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 21 | kJ/m² | |
| 23°C | 55 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 21 | kJ/m² | |
| 23°C | 52 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 60.0 mm Span) | 54.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 175 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 2502AH | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| TECHNYL® A R 218 V30 BLACK | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Bergamid™ A700 TM-YF | PolyOne Corporation | Nylon 66 | Bergamid™ |
| APEX® 3610-75 | Teknor Apex Company | PVC, Flexible | APEX® |
| Karina BLACK PVC COMPOUND 700D48/ 1-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |