LUBEMID A26 GK30 NATURAL
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBEMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iuextO_LUBEMID-A26-GK30-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PA6,6 first choice natural colour. With glass beads 30%. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 to 1.37 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 to 3500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 40.0 to 45.0 | MPa | |
| Break | 35.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/5 | ||
| Yield | 3.0 to 4.0 | % | |
| Break | 6.0 to 7.0 | % | |
| Flexural Modulus 1 | 2500 to 3000 | MPa | ISO 178 |
| Flexural Stress 2 | 80.0 to 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 to 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 20 to 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 35 to 45 | J/m | ASTM D256A |
| 23°C 3 | 25 to 35 | kJ/m² | ASTM D256 |
| 23°C | 2.0 to 3.0 | kJ/m² | ISO 180/A |
| 23°C 4 | 3.5 to 4.5 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 20 to 30 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 235 to 245 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 230 to 240 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 70.0 to 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 240 to 250 | °C | ISO 306/A120 |
| -- | 230 to 240 | °C | ISO 306/B120 |
| Melting Temperature | 250 to 265 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer V70H | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| Sumikon® FM-PB600 | Sumitomo Bakelite Co., Ltd. | Polyester, TP | Sumikon® |
| TUFNYL® RXXIC DU WHITE | SRF Ltd. | Nylon 66 | TUFNYL® |
| Fainplast PVC RK 740/OM | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Keliren® CM352L | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |